| To view the PDF document you require Adobe® Reader. To download the reader click here |
| Acrylated Resin |
| |
 |
PAL – 6108 X 60 |
ACRYLATED ALKYD RESIN |
|
 |
|
|
| PAL- 6108 X 60 Acrylated modified alkyd resin. It is developed for fast drying exterior / interior durable air drying coatings. It could be used as, hydroxyl functional base, in two pack urethane systems. Similarly, it could be cross linked with MF resin or blocked isocynates, at higher temperatures, in one pack stoving systems. |
|
| Features : |
- Cost effective versatile resin
- Very good compatibility with pure acrylic resins, chlorinated rubber resins, Polyurethane resins
- Quick drying with very good acid & alkali resistance
- Very good exterior durability
|
|
| Applications : |
|
- Excellent substitute for chlorinated rubber coatings
- Quick drying coatings with very good exterior durability for exterior structures such as pipelines, tanks etc. The durability could be boosted by imparting few parts of pure acrylic resin in paint formulations
- Paint formulator can develop excellent coatings for Ship side paints, Container coatings, low bake primers & Top coat for chasis
- Hydroxy terminated base resin for two pack polyurethane application for exterior coatings
|
 |
|
|
| Physical Properties : |
| Sr. No. |
Property |
Unit |
Specification |
| 1 |
Appearance |
Visual |
Light Yellow Viscous Liquid |
| 2 |
Colour (Gardner Scale) |
Gardner |
10 Max |
| 3 |
Viscosity in 40 % xylene @ 30° C |
Sec |
25 - 45 |
| 4 |
Specific Gravity @25° C |
gm/cm3 |
0.96 - 0.98 |
| 5 |
Flash point (Closed Cup) |
°C / °F |
28 / 82 |
| 6 |
N.V.M [1 hr @120° C] |
% |
60± 2 |
| 7 |
Hydroxy value (As such) |
MgKOH / g |
24 - 30 |
| 8 |
Hydroxy equivalent weight |
g / eq. |
2100 |
|
| |
| Curing Properties : |
| 1. |
Air drying systems |
|
| |
Recommended solvent
|
Xylene, C IX, Butanol. |
| |
Recommended Driers |
Ca, Co & Zr |
| |
Surface Dry |
10 min |
| |
Tack Free |
45 min |
| |
Hard dry |
Over Night |
| 2. |
Two pack urethane systems
|
|
| |
Recommended OH equivalent for two pack urethane systems |
2100 |
|
|
| Starting Formulations Based on PAL - 6108 X 60 (Acrylated Resin) : |
| I) Quick Drying Enamel : |
| Sr. No. |
Raw Material |
Percentage |
| 1 |
Titanium Dioxide |
20.00 |
| 2 |
Dispers BYK -110 |
0.20 |
| 3 |
PAL - 6108 X 60 |
60.00 |
| 4 |
CLP - 65% |
2.00 |
| 5 |
BYK - 410 |
0.60 |
| 6 |
Calcium Drier |
0.40 |
| 7 |
Cobalt Drier |
0.60 |
| 8 |
Zirconium Drier |
0.60 |
| 9 |
BYK -310 |
0.20 |
| 10 |
Xylene |
5.40 |
| 11 |
C - IX |
8.00 |
| 12 |
Butanol |
2.00 |
| Total |
|
100.00 |
|
|
| Paint Properties : |
| Specific Gravity : |
1.10 ± 0.04 kg / ltr |
| Viscosity : |
100 ± 20 Sec in B4 cup at 30° C |
| Drying Time : |
SD -20 Minutes
TD-120± 30 Minutes at ambient temperature |
| S.V.R. : |
35 |
|
|
|
| II ) Starting Formulation of Polyurethane Paint based on PAL-6108 x 60 & Aliphatic Isocynate |
| Base composition |
| Sr. No. |
Raw Material |
Percentage |
| 1 |
Titanium Rutile |
20.00 |
| 2 |
Dispersing Agent |
0.20 |
| 3 |
UV – Stabilizer |
0.20 |
| 4 |
PAL-6108 x 60 |
48.00 |
| 5 |
Slip Agent |
0.20 |
| 6 |
Thixotropic Agent 10 %
|
3.00 |
| 7 |
Xylene |
2.40 |
| 8 |
Butyl Acetate |
4.00 |
| 9 |
Solvent C-IX |
8.00 |
| 10 |
Ethyl Cellosolve Acetate |
4.00 |
| Hardener Composition |
| 11 |
Aliphatic Isocynate x 75 % |
4.25 |
| 12 |
Butyl Acetate
|
5.75 |
| |
Total |
100.00 |
|
|
|
| Paint Properties : |
| Specific Gravity : |
1.10 ± 0.04 kg / ltr |
| Viscosity : |
50 ± 20 Sec in B4 cupat30°c |
| Drying Time : |
SD - 15 ± 5 Minutes
TD- 120± 30 Minutes |
| Gloss at 60 deg |
72--76 |
| S.V.R. |
35 |
| Mixing Rratio |
Base : Hardener |
| |
9 part : 1 Part |
|
| |
| Handling & Storage : |
Handling: Avoid use of electric band heater or application of direct flame to container. It can cause explosion & fire.
Storage: Good general ventilation should be sufficient for most conditions. Local exhaust ventilation may be necessary for some operations. |
|
|